The moisture absorption behavior of flax fiber-reinforced epoxy composites is deliberated to be a serious issue. This property restricts their usage as outdoor engineering structures. Therefore, this study provides an investigation of moisture in flax fibers on the performance of the flax/epoxy composite materials based on their shear responses. The ±45° aligned flax fibers exposed to different relative humidities (RH) and the vacuum infusion process was used to manufacture the composite specimens. The optimum shear strength (40.25 ± 0.75 MPa) was found for the composites manufactured with 35% RH-conditioned flax fibers, but the shear modulus was reduced consistently with increasing RH values. Although shear strength was increased because of fiber swelling with increased moisture absorption rate until 35% RH environments with good microstructures, nonetheless, strength and modulus both started to decrease after this range. A very poor microstructure has been affirmed by the SEM images of the composite samples conditioned at 90% RH environments.
Development of environment-friendly natural fiber composites has been a recent trend. However, due to the fact that natural fibers permit high level of moisture absorption from the surroundings, it can lead to weak bindings and degradation of composite properties. This paper presents an experimental study on the dynamic performance of flax fiber composite beams manufactured at different relative humidity (RH) levels. Five types of flax fiber-reinforced composite materials were made under different RH values, i.e., dry, 35%, 50%, 70%, and 95% RH, and beam samples were prepared using the composite. Impact hammer testing was conducted to measure the natural frequencies and damping of the beams. It was found that for the first three modes, while the resonant frequencies are very close for most samples, there is a clear drop of frequencies for the composite fabricated at 95% RH. Along with an increase of the RH level, the damping ratios for all the three modes have reported a slight increase, but the variation is not significant.